Name: STAVITRODE A 74
Brand: Stanvac

STAVITRODO A 74

DESCRIPCIÓN Y APLICACIONES:

A basic coated hardfacing electrode usable in every position, for parts that suffer impact, compression and abrasive wear. It provides anti-wear protection on carbon steels and manganese steels.

Used for hardfacing and repairing ploughshares, crusher jaws, cutting tools, dipper teeth, bucket teeth and screw conveyors.

Welding technique: hold the electrode nearly vertical and keep the arc short; if required, re-dry for 2 hours at 300°C. Where the base is prone to cracking, put down a buffer layer of NiMnCr first. Low alloyed, high carbon tool steels need preheating anywhere from 200 - 400°C, depending on composition and thickness. After surfacing, let the part cool slowly in still air.

CARACTERÍSTICAS ÚNICAS:

Resists wear, abrasion, impact and compression.
Hardfacing in all positions, giving 60 - 63 HRC without treatment.
The basic coating yields a tough deposit that resists cracks.
Current: AC (50 V OCV) or DC (+).

Consulta

Detalles del producto

ESPECIFICACIONES CLAVE:

C	Si	Mn	Cr	V	Mo	B
0.50	1.00	1.00	8.50	1.80	1.50	0.20

ALL WELD METAL MECHANICAL PROPERTIES (TYPICAL) :

Hardness (HRC)
60 - 63 (without treatment)

RECOMMENDED WELDING CURRENT :

Diameter (mm)	Current (A)
3.15	90 - 120
4.00	140 - 170
5.00	180 - 210

Preguntas frecuentes

What is STAVITRODE A 74 used for?

STAVITRODE A 74 is a basic coated, all position hardfacing electrode for anti-wear work on carbon and manganese steels, covering hardfacing and repair of screw conveyors, bucket teeth, dipper teeth, cutting tools, crusher jaws and ploughshares.

How hard is the STAVITRODE A 74 deposit?

Typically 60 - 63 HRC with no treatment, and it resists impact, compression and abrasive wear.

What preheat does STAVITRODE A 74 require?

A buffer layer of Ferrowork NiMnCr is recommended on crack-sensitive materials. Low alloyed, high carbon tool steels have to be preheated to 200 - 400°C depending on composition and thickness, and cooled slowly in still air after surfacing.

What amperage should I set for STAVITRODE A 74?

Set 90 - 120 A for 3.15 mm, 140 - 170 A for 4.00 mm and 180 - 210 A for 5.00 mm, on AC (50 V OCV) or DC (+). If necessary, re-dry at 300°C for 2 hours.